Composition: It is composed of organic silicon resin, active antirust pigment, penetrating agent, curing agent, additives, etc.
Performance: This product not only has high temperature resistant performance, but also has excellent weather resistant, corrosion resistant performance. After high temperature treatment, the paint film can make the organic silicon and silicate minerals connect together, so as to protect the base material. This product has improved the poor corrosion resistance ability of former organic silicone coatings under normal temperature, high temperature and washing alternate cooling and heating state.
Application: Commonly used on the steel and cement surface under 600℃, to have the decoration, protection and anticorrosion functions. The coating can be used in exhaust pipe, grill, brazier, fireplace and other metal surface.
 |
 |
 |
Product specification
| Temperature resistant range | Paint film color | Coating types | Mixing proportion |
| 600℃ | gray | Primer | One-component, Dual-component |
| 600℃ | Black, white, grey, aluminum pink, and other colors | Finish paint | One-component, Dual-component |
Technical parameters
| Item | Index |
| Color | Primer: grayFinish: Black, white, grey, aluminum pink, and other colors |
| Luster | Primer: mattFinish: matt or semi-light |
| Viscosity | 25-60s（25±1℃, painting -4） |
| Drying time（23±2℃） | Primer: surface dry ≤1h, hard dry ≤24hFinish: surface dry ≤2h, hard dry ≤24h |
| Flexibility | ≤2mm |
| Adhesion | ≤2級 |
| Impact strength | ≥40kg·cm |
| Heat resistance（600℃，2h） | No foaming, no crack |
| Shelf life | 25℃, store for 6 to 12 months away from light |
Construction method
1、Base material processing
The coated base material surface must carry out thorough removal of grease, scale, rust, old coating, and etc., using shot or sand blasting method, to reach Sweden derusting standard Sa2.5 grade and roughness of 30-70μm, manual derusting methods can also be adopted to reach Sweden derusting standard St3 grade and roughness of 30-70μm.
2、Mixture (applicable for two-component paint)
According to the weight ratio (the label on the product packaging shall prevail).
When mixing, under the condition of stirring the main agent continuously, slowly pour in curing agent to make it fully ad evenly stirred.
20 min after curing of the well mixed coating, filter with 60-80mesh screen, and pour into another container for spare use.
The mixed coating is valid for 3 hours; please arrange the use according to the construction progress.
3、Baking (applicable for one-component paint)
| Product name | Baking temperature | Holding time |
| 600℃ Organic silicon heat resistant coating | 220℃ | 30min |
| 280℃ | 20min |
4、Construction conditions
Coating operation shall be performed as soon as possible after the substrate processing, generally not exceeding 8 hours. The substrate surface temperature and environmental temperature are generally no less than 10℃, the surface temperature shall be at least 3℃ higher than the dew point temperature, and the relative humidity of the air shall not exceed 85%.
5、Coating method
This coating can use brush coating, airless spraying and auxiliary air spraying method for construction.
6、Dilution
Generally the coating shall use the matching thinner to adjust viscosity and cleaning tools.
7、Coating intervals
One-component paint can carry out later coating after drying; two-component paint is suggested to have the coating time intervals as follows:
| Substrate temperature | 5℃ | 20℃ | 30℃ |
| Shortest | 48h | 24h | 12h |
| Longest | No limit | ||