Composition: It is two component self drying coating, which composed of acrylic resin, pigments, additives, fillers, solvents and other components
Performance: It has good atmospheric chemical resistance, kerosene and gasoline hydrocarbon solvent resistance and mechanical performance is excellent. The paint gloss can be adjusted, the film is full and beautiful.
 |
 |
|
Good weather resistance The paint can be in outdoor as long ultraviolet irradiation, paint film is not pulverization. |
Oil resistance The paint can be resistant to gasoline, kerosene, oil and hydrocarbon solvents, It is poor to resistant ester, ketone solvents. |
 |
 |
|
Excellent mechanical properties It has excellent adhesion, strong impact resisance and flexibility。 |
Beautiful decorative The paint gloss can be adjusted, the film is full and beautiful. |
Application: this paint can be applied to bridge, oil tank, container, steel structure, chemical pipeline, etc.
Product specification
Paint film color: specified by the customer
Mixing ratio: Flat products: main paint: curing agent=20:4
High optical products: main paint: curing agent=20:5
Technical parameters
| Item | Index |
| Non-volatile matter content | ≥60 |
| Fineness | ≤35μm |
| Bending | ≤2mm |
| Impact strength | 50kg.cm |
| Adhesion | ≤level 2 |
| Recoatability | accessible |
| Acid resistance（168h） | No bubbles, no abscission |
| Alkali resistance（168h） | No bubbles, no abscission |
| Cold and hot circulation （5 times） | No bubbles, no abscission |
| Salt spray resistance （800h） | No bubbles, no abscission |
Supporting system
Acrylic polyurethane paint can be applied to various industrial environments:
?Carbon steel, cast iron: epoxy zinc-rich primer, epoxy iron oxide red primer, epoxy zinc phosphate primer, inorganic zinc-rich primer
?Galvanized steel, stainless steel, aluminum alloy: stainless steel, galvanized sheet special primer, epoxy zinc chromate primer, etc
?Glass steel: Light grey epoxy primer
?Plastic (ABS): Direct use after surface treatment
?Concrete: epoxy sealing primer + epoxy micaceous iron oxide intermediate paint
Construction method
1、Base material processing
The coated base material surface must carry out thorough removal of grease, scale, rust, old coating, and etc., using shot or sand blasting method, to reach Sweden derusting standard Sa2.5 grade and roughness of 30-70μm, manual derusting methods can also be adopted to reach Sweden derusting standard St3 grade and roughness of 30-70μm.
2、Mixture
According to the weight ratio (the label on the product packaging shall prevail)
When mixing, under the condition of stirring the main agent continuously, slowly pour in curing agent to make it fully ad evenly stirred.
20 min after curing of the well mixed coating, filter with 60-80mesh screen, and pour into another container for spare use.
The mixed coating is valid for 3 hours; please arrange the use according to the construction progress.
3、Construction conditions
Coating operation shall be performed as soon as possible after the substrate processing, generally not exceeding 8 hours. The substrate surface temperature and environmental temperature are generally no less than 10℃, the surface temperature shall be at least 3℃ higher than the dew point temperature, and the relative humidity of the air shall not exceed 85%.
4、Coating method
This coating can use brush coating, airless spraying and auxiliary air spraying method for construction.
5、Dilution
Generally the coating shall use the matching thinner to adjust viscosity and cleaning tools.
6、Coating intervals
One-component paint can carry out later coating after drying; two-component paint is suggested to have the coating time intervals as follows:
| Substrate temperature | 5℃ | 20℃ | 30℃ |
| Shortest | 48h | 24h | 12h |
| Longest | No limit | ||